Paint | Approx Thick | Scratch Resistance | Corrasion Resistance | Heat Resistance | |
Salts | Moisture | ||||
polyester | 20 µ | 2800 gms | 500 hour | 1000 hour | 120 c |
pvdf | 27 µ | 3000 gms | 500 hour | 1000 hour | 120 c |
plastisol | 100 - 200 µ | 3500 gms | 1000 hour | 1000 hour | 60 c |
PVC film | 200 µ | 3500 gms | 1000 hour | 1000 hour | 60 c |
polyurethane | 50 µ | 3500 gms | 1000 hour | 1000 hour | 80 c |
backcoat | 10 µ | 2100 gms | - | 1000 hour | 120 c |
Plastisol 100-150-200 µ | ||
General Features |
Good stability in sunlight Very good formability Very good resistance to corrosion Excellent resistance to abrasion Fire resistance |
UK BS 476 |
Surface 'pencil' hardness | 4 - 6B | ASTM D 3363 ECCA T4 |
'BUCHHOLZ' hardness | 40 - 50 | |
'CRACK' limit radius | 1 - 3T | |
Impact resistance Salt spray TABER abrasion resistance |
Very good 1250 - 1750 hours for 275 Z or equivalent 25 mg |
ISO 7253 ECCA T8 ASTM D 4060 |
Temperature Resistance | 1 hour at 120 c 500 hour at 90 c 6 week at 75 c Class 1 |
BS 476 : part 7 IANSCO (France) |
Acid/Bases oil resistance Solvent resistance |
Good - very good Very good |
|
Mineral oil resistance Food certifcate |
Very good At request |
|
Coating thickness Coating composition |
5 + 15 Front : 5 µ anticorrosion primer + 15 µ super vinyl 303 Back : 7 µ nominal PU compatible backer in grey colour |
|
Temperature protection Paint retouching |
Paraffin Brush, spray gun or aerosol |
ISO 2813 ISO 7724 |